RS-100ä is an inorganic ceramic fiber reinforced laminate.
Has exceptional flexural and compressive strengths. Can be used in applications up to 2300°F (1260°C). It is inorganic, non-flammable, and can be used in direct contact with molten aluminum and other non-ferrous materials. It is not brittle and has high impact properties. RS-100TM can be used as low temperature kiln and oven walls; for induction furnace components such as channel melter components, coil liners, coreless induction components, coverts, tops, bases, front and back plates, coil supports and splash and coil shields; also, used in non-ferrous metal & glass industries. Can also be used as electrical insulation in high temperature areas. |
An inorganic, ceramic fiber reinforced structural alumina composite material.
|
24 x 48 and 36 x 36 in the following thicknesses in inches- 1/8, 3/16, 1/4, 3/8, 1/2, 3/4, and 1; cut and fabricated to shape |
Off-white |
|
|
|
|
Density |
130 lbs/ft3 (2100 kg/m3) |
|
Maximum operating temperature |
2300° F (1260º C) |
|
Shrinkage after 4 hrs @ 2200° F |
1 to 2% |
|
Compressive strength |
10,000 psi (69 Mpa) |
|
Modulus of rupture |
3000 psi (210Mpa) |
|
Durometer Hardness |
90 |
|
Moisture content at 220° F |
0-2% |
|
Volume resistivity |
7.2x 1011 ohm-cm |
|
Dielectric strength |
71 volts/mil |
|
Arc resistance |
> 420 sec |
RS-100ä is manufactured by Zircarâ Products, Inc