Non-combustible

Non-electrically conductive

Low thermal conductivity

High strength, corrosion and water resistant

Machinable

Uniform temperature control

Minimal maintenance

Marinite^TM I panels can be used in construction and refurbishment of ovens, dryers and other insulated housings for the retention of control or heat.   It, also, can be used in areas of fire protection, fire training, and as lightweight insulation panels

Marinite^TM I combines structural strength with high thermal insulating values. It is incombustible, highly damage resistant, non-corroding, and extremely water resistant. Mariniteā I panels also provide fire safety, uniform temperature control, and require minimal maintenance.

An oven dried, structural insulation board formed from calcium silicate with inert fibers and reinforcing agents

48 x 96 in the following thicknesses in inches- ½, ¾, 7/8, 1, 1 ¼, 1 ½, and 2; cut and fabricated to shape.

Off-white

Density

46 lbs/ft3 - 737 kg/m3

Maximum operating temperature

1200° F

Shrinkage, during initial heating condition

length & width

0.4%

thickness

1.4%

Compressive strength - for 10% deformation

1350 psi

Flexural strength

800 psi (56 kg/cm2)

Pandux, Durometer Hardness

60

Normal moisture content

3%

Thermal Conductivity

.81 BTU-in/ft²,hr,° F@400° F (0.12W/mK@205° C)

.86 BTU-in/ft²,hr,° F@1000° F (0.12W/mK@538° C)

Fire hazard(ASTM 84) flame spread

0

smoke developed

0

Volume resistivity (ASTM D-257)

600° F - dry

8.15 x 1011 ohm-cm

75° F - 50% relative humidity

9.83 x 107 ohm-cm

71° F - 91% relative humidity

3.49 x 106 ohm-cm

Dielectric strength (ASTM D-495)

45 volts/mil

Screw holding strength @7/8in penetration

220 lbs (100kg)