MariniteTM P is a structural insulation board formed from calcium silicate with inert fibers and reinforcing agents.

 

 

[Bullet] Structural strength with high thermal insulating  
                values
[Bullet] Excellent resistance to compression
[Bullet] High tensile, shear and transverse strengths
[Bullet] Will not decay or rust
[Bullet] Incombustible, highly damage resistant,
[Bullet] Water resistant
[Bullet] Will not mold when exposed to prolonged dampness
[Bullet] Provides fire safety, uniform temperature control
[Bullet] Minimal maintenance
[Bullet] Machinable
[Bullet] Non-corroding

Suited to withstand temperature/ pressures associated with platen press operations Durable, low maintenance insulation for large diameter pipe support systems in the power generation and process industries.
Ceramic and foundry applications - used as a pallet to support special refractory shapes and foundry cores during oven drying

Ideal for backup insulation in rotary kilns in lime and cement plants, steel ladles, torpedo cars and tundishes in steel plants

 

An oven dried, structural insulation board formed from calcium silicate with inert fibers and reinforcing agents.

 

 

48 x 96 in the following thicknesses in inches- 1/2, 3/4, 1, 1 1/2 and 2; cut and fabricated to shape by Taylored Industries.

Off-white

 

MariniteTM P combines structural strength with high thermal insulating values. This insulation offers excellent resistance to compression as well as high tensile, shear, and transverse strengths. The material will not decay or rust. It is incombustible, highly damage resistant, non-corroding, and extremely water resistant. MariniteTM P panels also provide fire safety, uniform temperature control, minimal maintenance; and it is machinable.

 

 

Density

 60 lbs/ft3 - 961 kg/m3

Maximum operating temperature

 1200° F (649º C)

Shrinkage, during initial heating condition

  

  length & width

 0.6%

  thickness

 2.1%

Compressive strength - for 10% deformation

 3050 psi

Modulus of rupture

 1400 psi (98Kg/cm2

Pandux, Durometer Hardness

  
  Die side 75
  Screen Side 78
Normal moisture content 3%

Thermal Conductivity

 1.13 BTU-in/ft2,hr,° F@ 400° F (0.16W/mK@ 205° C)
  1.17 BTU-in/ft2,hr,° F@ 1000° F (0.17W/mK@ 538° C)

Fire hazard(ASTM 84) flame spread

  

  flame spread

 0
  smoke developed 0

Volume resistivity (ASTM D-257)

 5.0 x 108 ohm-cm

Dielectric strength (ASTM D-495)

 46 v/mil

Screw holding strength @7/8in penetration

 500 lbs (227kg)

Marinite TM P is manufactured by BNZ Materials, Inc.